Analysis of basic related knowledge of lightweight mullite brick

The main crystalline phase of the lightweight mullite brick is an aluminum-silicon-based insulating refractory brick of mullite phase. Light mullite bricks are classified into MG-23, MG-25, MG-26, MG-27, MG-28, MG-30 and MG-32 according to the classification temperature, for a total of seven grades. Among them, M and G are Mo, the first letter of Chinese Pinyin, and the subsequent numbers represent the classification of mullite insulation refractory bricks.
 
The raw materials for the production of lightweight mullite bricks mainly use refractory products with kyanite as the main raw material because the kyanite forms many micropores between the particle skeletons during the decomposition and expansion process. For refractory articles that are in direct contact with the melt, the presence of these micropores reduces their erosion resistance. Light mullite bricks are used for the lining of high temperature furnaces that are not in contact with the melt. They are required to have high operating temperatures and low thermal conductivity. For a general lightweight refractory material, the smaller the pore size is, the lower the thermal conductivity is within a certain range. Therefore, the micropores formed by the decomposition and expansion of kyanite are favorable conditions for improving the thermal insulation performance of lightweight mullite bricks. The ideal chemical composition of mullite is 3AL2O3·2SiO2, of which AL2O3 accounts for 71.8% and SiO2 accounts for 28.2%. Its melting point is 1910 ° C, which is the mineral phase of the aluminum silicate system next to corundum (melting point 2050 ° C). Therefore, the lightweight mullite brick with mullite as the main crystal phase has a high use temperature. If the kyanite is completely converted to mullite during the decomposition process, alumina must be added to the ground kyanite powder.
 
In order to make the lightweight mullite bricks have a sufficiently high mullite content, and at the same time, the product can be sufficiently sintered within a relatively easy temperature range, the content of the light mullite brick AL2O3 is 67.1, slightly Low with the ideal composition of mullite.
 
Lightweight mullite refractory bricks have the characteristics of high use temperature, low heat capacity, low thermal conductivity, high strength and good thermal shock resistance. The light mullite brick with 65% of AL2O3 synthesized by kyanite and industrial alumina powder is mainly used in various kiln for daily-use ceramics, architectural ceramics and special industrial ceramics, various high temperatures in the petrochemical industry. Kiln, various high-grade heating furnaces and large-scale hot-blast stoves in the metallurgical industry are used for direct refractory lining. In these kiln, when the working temperature exceeds the temperature that other lightweight materials can withstand (such as refractory fibers), and the parts that must use lightweight materials can fully exert the various properties of the lightweight refractory bricks.